INDUCTOTHERM MELTING DIVISION
|
|
VIP POWER - TRAK R/CR의 보증 용해속도(Kg/Hr)
(200Hz-3000Hz) |
HZ |
VIP SIZE(KW) |
STEEL@1630'C |
BRONZE@1175'C |
IRON@1480'C |
3000
|
75 |
100 |
180 |
110 |
125 |
185 |
350 |
205 |
175 |
270 |
515 |
300 |
225 |
375 |
680 |
405 |
325 |
570 |
1045 |
635 |
1000 |
150 |
225 |
430 |
245 |
200 |
315 |
610 |
345 |
250 |
430 |
815 |
475 |
300 |
530 |
1000 |
590 |
350 |
625 |
1180 |
680 |
400 |
725 |
1380 |
800 |
450 |
810 |
1540 |
900 |
500 |
900 |
1725 |
1000 |
600 |
1090 |
2060 |
1200 |
* 750 |
1430 |
2720 |
1575 |
* 1000 |
1900 |
3625 |
2100 |
* 1250 |
2380 |
4535 |
2625 |
* 1500 |
2860 |
5440 |
3150 |
200
AND
500 |
350 |
625 |
1180 |
680 |
500 |
900 |
1725 |
1000 |
600 |
1090 |
2060 |
1200 |
* 750 |
1430 |
2720 |
1575 |
* 1000 |
1900 |
3625 |
2100 |
* 1250 |
2380 |
4535 |
2625 |
* 1500 |
2860 |
5440 |
3150 |
* 1750 |
3340 |
6345 |
3675 |
* 2000 |
3820 |
7250 |
4200 |
* 2500 |
4770 |
9070 |
5250 |
* 3000 |
5725 |
10880 |
6300 |
* 3500 |
6680 |
12695 |
7350 |
* 4000 |
7635 |
14510 |
8400 |
* 5000 |
9545 |
18130 |
10500 |
* 6000 |
11460 |
21950 |
12600 |
* 7000 |
13360 |
25390 |
14700 |
* 8000 |
15270 |
29020 |
16800 |
* 9000 |
17180 |
32630 |
18900 |
* 10000 |
19090 |
36260 |
21000 |
100 |
* 12000 |
. |
43500 |
25200 |
* 15000 |
. |
54390 |
31500 |
* 20000 |
. |
. |
42000 |
* 25000 |
. |
. |
52500 |
|
|
- 출탕을 끝낸 후 용해로가 가열된 상태에서 깨끗한 재료로 양호하게 빈틈없이 장입하여 용해했을
때 얻을 수 있음.
- 타 금속의 경우는 강(STEEL) 용해속도에 다음의 수를 곱함 알루미늄-1.0, 동-1.6, 금-5.0, 은-2.85
- 진공하의 용해속도는 대기용해의 경우보다 5~10% 떨어짐 (* VIP PI UNIT) |
|
|
최적 회로설계
- 최고 효율에 의한
최저 전력 원단위
- 투입 전력에 관계
없이 항상 역율
95%이상
- 고조파 발생 극소
|
|
|
|
동력공급장치 